Due to the addition of Mo element, 316 stainless steel corrosion resistance, and high temperature strength has a greater improvement, high temperature resistance can reach 1200-1300 degrees, can be used in the harsh conditions
Application: seawater equipment, chemical, dye, paper, oxalic acid, fertilizer and other production equipment;Photography, food industry, coastal facilities, ropes, CD sticks, bolts, nuts.
Welding
Excellent weldability by all standard fusion and resistance methods, both with and without filler metals. Heavy welded sections in Grade 316 require post-weld annealing for maximum corrosion resistance. This is not required for 316L.
316L stainless steel is not generally weldable using oxyacetylene welding methods.
Machining
316L stainless steel tends to work harden if machined too quickly. For this reason low speeds and constant feed rates are recommended.
316L stainless steel is also easier to machine compared to 316 stainless steel due its lower carbon content.
Hot and Cold Working
316Lstainless steel can be hot worked using most common hot working techniques. Optimal hot working temperatures should be in the range 1150-1260°C, and certainly should not be less than 930°C. Post work annealing should be carried out to induce maximum corrosion resistance.
Most common cold working operations such as shearing, drawing and stamping can be performed on 316 stainless steel. Post work annealing should be carried out to remove internal stresses.
Hot-Rolled Stainless Steel Plate:
Continuous casting slab or slab slab is used as raw material, heated by step heating furnace, dewatered by high pressure water and then into rough rolling mill. The rough rolling material passes through the cutting head and tail and then enters the finishing mill to carry out computer controlled rolling. After the final rolling, it is subjected to laminar cooling (computer controlled cooling rate) and coiler winding, which becomes a straight hair roll. The head and tail of the straight hair roll are often in the shape of a tongue and a fishtail. The thickness and width are poorly accurate, and the side has frequent defects such as a wave shape, a folded edge, and a tower shape. The weight of the coil is heavier and the inner diameter of the coil is 760 mm.
| Hot rolled plate |
Specification
(Thick) | Big Deviation | Normal Deviation | Small Deviation | No Deviation |
| 3.0mm | 2.6mm-2.75mm | 2.75mm-2.85mm | 2.86mm-2.9mm | no less than 2.9mm |
| 4.0mm | 3.5mm-3.6mm | 3.6mm-3.75mm | 3.76mm-3.95mm | no less than 3.95mm |
| 5.0mm | 4.5mm-4.6mm | 4.6mm-4.75mm | 4.75mm-4.95mm | no less than 4.95mm |
| 6.0mm | 5.4mm-5.6mm | 5.6mm-5.75mm | 5.75mm-5.85mm | no less than 5.85mm |
| 8.0mm | 7.3mm-7.5mm | 7.5mm-7.65mm | 7.65mm-7.85mm | no less than 7.85mm |
| 10.0mm | 9.2mm-9.3mm | 9.3mm-9.6mm | 9.6mm-9.85mm | no less than 9.85mm |
| 12.0mm | 11.1mm-11.2mm | 11.2mm-11.6mm | 11.6mm-11.85mm | no less than 11.85mm |
| 14.0mm | 13.1mm-13.2mm | 13.2mm-13.6mm | 13.6mm-13.85mm | no less than 13.85mm |
How Can You Ship Goods Like Heavy welded Stainless Steel pipe. What Is Best Pacakge?
- Packing is quite important especially in a case of international shipments in which consignment pass through various channels to reach the ultimate destination, so we put special concern regarding packaging.
- We pack our goods in numerous ways based on the products. We pack our products in multiple ways, such as,
- Waterproof paper reinforcement of steel strip
- Kraft paper
- Carton boxes
- Wooden pallets
- Wooden boxes
- Wooden crates
-