Low Carbon Steel Sae 1045 Steel Channel For Structure
AISI 1045 Carbon Steel Angle has a low corrosion rate in rapidly flowing brackish or seawater combined with excellent resistance to stress – corrosion cracking in most freshwaters. The resistance to a variety of corrosive conditions in our AISI 1045 Carbon Steel C-Channel led to its wide use in marine applications and other non – oxidizing chloride solutions. As would be expected from its high copper content, this AISI 1045 Carbon Steel Chain is rapidly attacked by nitric acid and ammonia systems. This type of failure in our AISI 1045 Carbon Steel I-Beam is generally associated by means of an environment containing chlorides as well as with stress, water, dissolved oxygen, and other factors. The tendency of austenitic alloys to crack trans – granularly in chloride solutions decreases as the nickel content of our AISI 1045 Carbon Steel H-Beam is increased. These AISI 1045 Carbon Steel T-Beam offer faster machining speeds, longer tool life, improved part quality, and lower total cost of machined parts. Our AISI 1045 CS Angle is forged between 2250 Degree F / 1750 Degree F (1230 Degree C / 955 Degree C) following a soak at forging temperature of 30 minutes per inch of billet or ingot section thickness.
| Product name |
Lightweight low carbon steel channel for structure |
| Size |
Side Length |
20-1000mm |
| W.T |
0.2-30mm |
| Length |
1-12m |
| Standard |
AISI,ASTM,GB,DIN,BS,JIS |
| Grade |
16Mn STS49 STPT49 G3455 G3456 A210 st52.4 st52 A333 DIN1629/3 DIN1629/4,Q345-b |
| Inspection |
X-ray inspection, manual ultrasopic inspection,surface inspection,hydraulic testing |
| Technique |
Hot Rolled |
| Section Shape |
square |
| Main Market |
Southeast Asia, Middle East, Australia,USA,South America,Africa |
| Productivity |
5000 Tons/month |
| Packing |
Standard bundle package Beveled end or as per request |
| Surface Treatment |
Black Painted, PE Coated, Galvanized or Customized all available |
| Date of Delivery |
According to The Specifications And the Quantities Of Each Contract,
Time Start To Begin When We confirm the Date of the Earnest or L/C |
| Method of Payment |
T/T L/C West Union |
| Method Of Delivery |
Terms According To the <INCOTERMS 2000> for International Trading |
| Remarks |
1.Payment Terms T/T, L/C,West Union |
| 2.Trade Term:FOB/CFR/CIF |
| 3.Minimum Quantity of Order: 2 Tons |
| 4.Delivery Time:7-15 days after receipt of deposit |
AISI 1045 Steel is medium tensile steel supplied in the black hot rolled or normalized condition. It exhibits good weldability, good machinability, and high strength and impact properties to be used in various industrial applications.
AISI 1045 steel has a low through-hardening capability that recommended for tempering and through-hardening. Carbon steel AISI 1045 is a medium carbon, medium tensile steel supplied as forged or normalized. This steel shows reasonable strength and toughness. 1045 is the designation in both the SAE and AISI systems for this material. G10450 is the UNS number.
SAE 1045 Steel is used extensively by all industry sectors for applications requiring more strength and wear resistance than low carbon mild steels.
CHEMICAL COMPOSITION OF AISI 1045 STEEL
| AISI 1045 |
C |
Mn |
P |
S |
Fe |
| min |
0.43 |
0.60 |
– |
– |
Balance |
| max |
0.50 |
0.90 |
0.04 |
0.05 |
Balance |
PHYSICAL PROPERTIES OF CS AISI 1045 STEEL
| Properties |
Metric |
Imperial |
| Density |
7.87 g/cm3 |
0.284 lb/in3 |
AISI 1045 STEEL MECHANICAL PROPERTIES
| Properties |
Metric |
Imperial |
| Tensile strength |
585 MPa |
84800 psi |
| Yield strength |
450 MPa |
65300 psi |
| Modulus of elasticity |
200 GPa |
29000 ksi |
| Shear modulus (typical for steel) |
80 GPa |
11600 ksi |
| Poisson’s ratio |
0.29 |
0.29 |
| Elongation at break (in 50 mm) |
12% |
12% |
| Hardness, Brinell |
163 |
163 |
| Hardness, Knoop (converted from Brinell hardness) |
184 |
184 |
| Hardness, Rockwell B (converted from Brinell hardness) |
84 |
84 |
| Hardness, Vickers (converted from Brinell hardness) |
170 |
170 |
CS AISI 1045 STEEL THERMAL PROPERTIES
| Properties |
Metric |
Imperial |
| Thermal conductivity |
51.9 W/mK |
360 BTU in/hr.ft2.°F |
| Thermal expansion coefficient (@0.000-100°C/32-212°F) |
11.2 µm/m°C |
6.22 µm/m°C |
EQUIVALENT GRADES OF AISI 1045 STEEL
| Grade |
UNS |
| AISI 1045 |
G10450 |
APPLICATIONS OF CARBON STEEL AISI 1045 STEEL
| Bolts |
Studs |
| Gears |
Axles |
| Shafts |
Machine parts |
Product Tags:
|
|